PolySonic™ PLA Pro is a high-performance, tough PLA engineered for industrial-grade productivity. It combines lightning-fast extrusion rates with the rugged durability required for functional parts. With impact strength comparable to ABS and bending strength that outperforms ASA and PETG, PolySonic™ PLA Pro is the ultimate solution for rapid manufacturing without structural compromise.
The "High-Speed" Standard: To be classified as PolySonic™, this material meets three rigorous criteria:
1. Flowability: Consistent extrusion at 24mm³/s.
2. Formability: Maintains surface quality and bridging integrity at top speeds.
3. Functionality: Retains over 80% of mechanical properties (layer adhesion and impact strength) even when pushed to its limits.
The Pro Advantage
Rugged Durability: Maintains 85% of its impact strength (19.4 kJ/m²) even at high-speed flow rates.
Superior Surface Quality: Specially formulated to prevent "Shark Skin" (gloss/matte variations), ensuring a consistent finish from 0mm/s up to 300mm/s.
Incredible Throughput: Optimized for modern high-speed platforms, reaching flow rates equivalent to 600mm/s at 0.1mm layer heights.
Consistent Mechanics: Retains 95% of its tensile strength and layer adhesion when transitioning from classic to high-speed printing.
Recommended Print Settings
Attribute
Classic Printing
High-Speed Printing
Extruder Temperature
190°C – 230°C
210°C – 230°C
Printing Speed
50 – 100mm/s
100 – 300mm/s
Bed Temperature
25°C – 60°C
Cooling Fan
ON
Technical Specifications
Direct Drive: 1mm Distance | 20mm/s Speed
Indirect (Bowden): 3mm Distance | 40mm/s Speed
Drying Settings: 55°C for 6 hours (if moisture is absorbed).