Nylon PA12 is a premier choice in industrial 3D printing for both functional prototyping and rugged end-use parts. It provides outstanding mechanical properties while saving development time and manufacturing costs through extensive design flexibility.
Reinforced with a 15% carbon fiber blend, its structural rigidity, chemical resistance, and tensile strength are significantly elevated. This premium PA12+CF composite delivers enhanced printability, superior dimensional stability, and minimal thermal shrinkage—making it an engineering favorite for advanced robotics, drone frames, automotive assemblies, and aerospace components.
Note on Abrasion: Due to the abrasive nature of carbon fibers, this filament will rapidly degrade standard 0.4mm brass nozzles. We strongly advise utilizing a hardened steel or wear-resistant nozzle with a larger diameter (0.6mm or greater). For maximum interlayer bonding and a clean surface finish, dry the filament prior to use and print within an enclosure or stable ambient temperature.
Reinforced with a 15% carbon fiber blend, its structural rigidity, chemical resistance, and tensile strength are significantly elevated. This premium PA12+CF composite delivers enhanced printability, superior dimensional stability, and minimal thermal shrinkage—making it an engineering favorite for advanced robotics, drone frames, automotive assemblies, and aerospace components.
Note on Abrasion: Due to the abrasive nature of carbon fibers, this filament will rapidly degrade standard 0.4mm brass nozzles. We strongly advise utilizing a hardened steel or wear-resistant nozzle with a larger diameter (0.6mm or greater). For maximum interlayer bonding and a clean surface finish, dry the filament prior to use and print within an enclosure or stable ambient temperature.
Exceptional Mechanical Performance
- Advanced Engineering Formulation: Composed of 85% Nylon PA12 and 15% high-rigidity Carbon Fiber.
- Ultra-Low Hygroscopicity: Superior resistance to moisture absorption compared to standard nylons, making it highly reliable in humid environments.
- Industrial Strength: Drastically increased structural stiffness, impact durability, and wear resistance.
- Flawless Printability: Formulated for low shrinkage and zero warping, yielding tight layer adhesion and a sleek matte finish.
- Dimensional Accuracy: Excellent tolerances for complex structural assemblies.
Printing Tips & Guidelines
- Extruder/Nozzle Temperature: 280°C - 300°C (536°F - 572°F)
- Heated Bed Temperature: 45°C - 60°C (113°F - 140°F)
- Print Speed Range: 40 - 100 mm/s
- Part Cooling Fan Speed: 0% (Turned off for maximum layer strength)
- Nozzle Requirement: Hardened steel, ruby, or stainless steel tip (0.6mm or larger recommended)
Material & Thermal Properties
- Melt Flow Index: 8.91 g/10min (270°C / 2.16kg)
- Density: 1.24 g/cm³
- IZOD Impact Strength: 11.33 kJ/m²
- Tensile Strength: 108.18 MPa
- Elongation at Break: 9.02%
- Flexural Strength: 116.58 MPa
- Flexural Modulus: 3335 MPa
- Heat Distortion Temperature (HDT): 94.1°C
- Continuous Service Temperature: 120°C
- Maximum Short-Term Use Temperature: 160°C